Ni80Cr20 waa nikkel-chromium alloy (NiCr alloy) oo lagu garto iska caabin sare, caabbinta oksaydhka wanaagsan iyo xasilloonida qaab aad u wanaagsan. Waxay ku habboon tahay in lagu isticmaalo heerkul ah ilaa 1200 ° C, waxayna haysaa nolol adeeg heer sare ah marka loo eego birta chromium aluminium alloys.
Codsiyada caadiga ah ee Ni80Cr20 waa walxo kuleyliyaha korantada ee qalabka guriga, foornooyinka warshadaha iyo iska caabiyeyaasha (iska caabinta wirewound, caabiyeyaasha filimka birta ah), birta fidsan, makiinadaha feeraha, kuleyliyaha biyaha, caagagga wax lagu dhejiyo ayaa dhinta, biraha alxanka, walxaha tuubada galka leh iyo walxaha kartoonada.
Halabuurka caadiga ah%
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Mid kale |
| Max | |||||||||
| 0.03 | 0.02 | 0.015 | 0.60 | 0.75 ~ 1.60 | 20.0-23.0 | Bal. | ugu badnaan 0.50 | ugu badnaan 1.0 | - |
Guryaha Makaanikada ee caadiga ah (1.0mm)
| Xoog soo saar | Xoogga Jilicsan | Dheeraynta |
| Mpa | Mpa | % |
| 420 | 810 | 30 |
Tilmaamaha Jireed ee caadiga ah
| Cufnaanta (g/cm3) | 8.4 |
| Iska caabin koronto oo ah 20ºC(mm2/m) | 1.09 |
| Isku-dheellitirnaanta hab-dhaqanka ee 20ºC (WmK) | 15 |
| Isku-dhafka ballaarinta kulaylka | |
| Heerkulka | Isku-dhafka Balaadhinta kulaylka x10-6/ºC |
| 20ºC-1000ºC | 18 |
| Awood kuleyl gaar ah | |
| Heerkulka | 20ºC |
| J/gK | 0.46 |
| Barta dhalaalka (ºC) | 1400 |
| Heerkulka hawada ee joogtada ah ee ugu badan (ºC) | 1200 |
| Guryaha magnetic | aan magnet ahayn |
| Qodobbada Heerkulka ee Cadaadiska Korontada | |||||
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 600ºC |
| 1 | 1.006 | 1.012 | 1.018 | 1.025 | 1.018 |
| 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1300ºC |
| 1.01 | 1.008 | 1.01 | 1.014 | 1.021 | - |
Habka sahayda
| Alloys Magaca | Nooca | Cabirka | ||
| Ni80Cr20W | Silig | D=0.03mm~8mm | ||
| Ni80Cr20R | Ribbon | W=0.4~40 | T=0.03~2.9mm | |
| Ni80Cr20S | Xarig | W=8 ~ 250mm | T=0.1~3.0 | |
| Ni80Cr20F | Fool | W=6 ~ 120mm | T=0.003~0.1 | |
| Ni80Cr20B | Baar | Dia=8~100mm | L=50~1000 | |