Sharaxaadda Badeecada

6J13 Manganin Daawaha Xarig

Dulmar Guud oo ku saabsan Badeecada

6J13 xarigga daawaha manganin, oo ah badeeco isku-dhafan oo iska caabin sare leh oo si madax-bannaan u soo saartay oo ay soo saartay Tankii Alloy Material, waa daawad iska caabin sax ah oo ku salaysan naxaasta-manganese-nickel (Cu-Mn-Ni). Waxaa lagu sameeyay iyada oo loo marayo dhalaalinta faakuumka ee horumarsan, duubista qabow ee badan, iyo hababka xakamaynta ee jawiga, xarigani wuxuu gaaraa dulqaad cabbir oo aad u adag iyo sifooyin koronto oo joogto ah. Waxay isku daraysaa faa'iidooyinka asaasiga ah ee daawadaha manganin:iska caabin sare oo deggan, Isku-dhafka heerkulka iska caabbinta hooseeya (TCR), iyoiska caabin daxalka aad u fiican— taasoo ka dhigaysa agabka ugu habboon ee iska caabbinta xasilloonida sare leh, shunt-ka hadda jira ee saxda ah, iyo qaybaha cabbiraadda korantada ee qalabka warshadaha, elektaroonigga baabuurta, iyo goobaha qalabka saxda ah.

Tilmaamaha Heerka iyo Aasaaska Agabka

Faa'iidooyinka Muhiimka ah (marka la barbar dhigo Alloys-ka Iska caabinta Guud)

Xarigga manganin-ka 6J13 wuxuu u taagan yahay waxqabadkiisa saxda ah ee dheellitiran iyo hab-socodkiisa:

Iska caabbinta waxaa si joogto ah loogu hayaa 0.44±0.04 μΩ·m (20℃), celceliska isku-dhafka heerkulka iska caabbinta (TCR) wuxuu u dhexeeyaa -20×10⁻⁶/℃ ilaa +20×10⁻⁶/℃ gudaha -50℃ ilaa 150℃, taas oo ka hooseysa kan joogtada ah (6J40: ±40×10⁻⁶/℃). Ka dib 1000 saacadood oo shaqo ah 120℃, iska caabbinta ayaa ka yar 0.01%, taasoo hubinaysa saxnaanta cabbirka muddada dheer ee qalabka saxda ah.

Qaab-dhismeedka isku midka ah ee birta (cabirka hadhuudhka ≤25μm) wuxuu suurtogaliyaa waxqabad shaqo oo qabow oo aad u fiican. Marka uu qaboobo nus-adag, xooggiisa jiidista wuxuu gaaraa 550-650 MPa, dhererkiisuna waa 15-20%, kaas oo u adkeysan kara shaambadda iyo foorarsiga saxnaanta sare (radius-ka laablaabashada ugu yar ≥2× dhumucdiisa) iyada oo aan la dillaacin. Dusha sare ee dhalaalaya ee la jeexjeexay (Ra ≤0.2μm) waxay ku habboon tahay xoqidda kiimikada aadka u fiican, iyadoo ugu yaraan ballaca xariiqda la xardhay uu yahay 0.03mm.

Nidaamka daawaha Cu-Mn-Ni wuxuu sameeyaa filim cufan oo aan firfircoonayn, kaas oo iska caabin kara daxalka jawiga, biyaha macaan, iyo jawiga kiimikada ee khafiifka ah (pH 4-10). Wuxuu ka gudbaa tijaabada buufinta milixda ASTM B117 1000-saacadood ah isagoon lahayn daxal muuqda. Dhanka kale, wuxuu leeyahay awood kuleyl oo hooseeya (≤2μV/℃ vs. naxaas), taasoo si wax ku ool ah u yareynaysa faragelinta cabbirka ee wareegyada danab-yaraanta.

Marka la barbardhigo daawaha manganin ee 6J12 (iska caabinta 0.47±0.03 μΩ·m), 6J13 waxay leedahay iska caabin yar oo hooseeya laakiin isku dheelitirnaan dufcadeed oo deggan iyo kharash wax soo saar oo hooseeya. Waa doorasho kharash-ool ah oo loogu talagalay qaybaha iska caabinta saxda ah ee dhexdhexaadka ilaa sare, iyadoo la isku dheelitirayo waxqabadka iyo dhaqaalaha.

Tilmaamaha Farsamada

Sifada	Qiimaha (Caadi ahaan)
Halabuurka Kiimikada (wt%)	Cu: 82.0-86.0% (余量); Mn: 12.0-13.0%; Ni: 2.0-3.0%; Fe: ≤0.5%; Si: ≤0.15%; C: ≤0.10%
Dhumucda	La habeyn karo: 0.05mm-2.0mm (dulqaad: ±0.002mm)
Ballaca	La habeyn karo: 10mm-300mm (dulqaad: ±0.1mm)
Dhererka Duubkiiba	50m - 300m (dherer la jaray ayaa la heli karaa: ≥100mm)
Iska caabin (20℃)	0.44±0.04 μΩ·m
Isku-darka Heerkulka ee Iska-caabbinta (TCR)	-20×10⁻⁶/℃ ilaa +20×10⁻⁶/℃ (-50℃ ilaa 150℃)
Awoodda Heerkulka Korontada (marka loo eego Cu)	≤2 μV/℃ (0℃ ilaa 100℃)
Heerkulka Hawlgalka Kala Duwan	-50℃ ilaa 120℃ (si joogto ah); Waqti gaaban: ilaa 150℃ (≤1 saac)
Xoogga Tijaabada	Jilicsan (la qaboojiyey): 450-550 MPa; Badh-adag: 550-650 MPa; Adag: 650-750 MPa
Kordhinta (25℃)	Jilicsan: ≥25%; Badh-adag: 15-20%; Adag: ≤10%
Adkaanta (HV)	Jilicsan: 130-150; Badh-adag: 180-200; Adag: 230-250
Qalafsanaanta Dusha Sare (Ra)	≤0.2μm (dhammaystir dhalaalaya oo la dubay)

Qeexitaannada Badeecada

Shay	Faahfaahinta
Dhammaadka Dusha Sare	Bilicsan oo dhalaalaya (aan oksaydh lahayn, aan saliid lahayn) - ugu habboon in si sax ah loo qodo; dhammaystir matte ah (la habeyn karo)
Fidsanaan	≤0.05mm/m - waxay hubisaa habaynta isku midka ah iyo isku dheelitirnaanta iska caabbinta
Mashiinka wax lagu farsameeyo	La jaan qaadaya shaambadda CNC, jarista laysarka, iyo qodista kiimikada; ma jiraan burrs gees ah ka dib marka la farsameeyo
Alxanka	Ku habboon alxanka booska iyo alxanka TIG - kala-goysyada alxanka leh waxay leeyihiin kala duwanaansho iska caabin ah ≤0.1%
Baakad	Faakiyuum lagu shaabadeeyay bacaha aluminium-ka ka hortagga oksaydhka oo leh qalajiyeyaal; alwaaxyo wareegsan (dhexroor 150mm ah) si looga hortago isbeddelka
Habayn	Hagaajinta heerkulka (jilicsan/badh-adag/adag); jarista ballaca; daawaynta ka hortagga wasakhaynta; qaababka ka hor-qoynta

Codsiyada Caadiga ah

Tankii Alloy Material waxay hirgelisaa xakamaynta tayada adag ee xariijimaha birta ah ee manganin 6J13: dufcad kasta waxay martaa falanqaynta halabuurka kiimikada XRF, tijaabada TCR ee saxsan (tijaabiyaha iska caabbinta heerkulka oo leh saxnaan ±0.1 ppm/℃), kormeerka cabbirka laysarka, iyo tijaabada xasilloonida kulaylka 1000-saacadood. Muunado bilaash ah (100mm × 100mm) iyo warbixinnada tijaabada walxaha oo faahfaahsan (MTR) ayaa la heli karaa marka la codsado. Kooxdayada farsamada waxay bixisaa taageero loo habeeyay - oo ay ku jiraan hagaajinta halbeegga birta iyo xulashada heerkulka ee hababka shaambadaynta - si ay uga caawiso macaamiisha inay kordhiyaan waxqabadka 6J13 codsiyada saxda ah.